Table 1: The calculated parameters in statistic thermodynamic model for La20.5MgNi78.5 and La15.5Mg6Ni78.5.
Samples | Process | T(K) | Eα(eV) | Eβ(eV) | χα(eV) | χβ(eV) | χαβ(eV) | L(eV) | xα | xβ | xβ- xα | Pm(Mpa) | ΔH(kJ/mol) | ΔS(J/K/mol) |
La20.5MgNi78.5 | Absorption | 303 | 0.0155 | –0.0366 | 0.0409 | 0.00985 | 0.0277 | 0.0336 | 0.287 | 0.826 | 0.539 | 0.1814 | –31.64 | –109.30 |
| | 318 | 0.0270 | 0.0431 | 0.0313 | –0.0785 | –0.2176 | 0.0051 | 0.292 | 0.821 | 0.530 | 0.3248 | | |
| | 333 | 0.0428 | 0.0754 | 0.0074 | –0.1089 | –0.2914 | –0.0032 | 0.301 | 0.810 | 0.510 | 0.5622 | | |
| Desorption | 303 | –0.0116 | 0.0742 | 0.0665 | –0.1328 | –0.2991 | –0.0196 | 0.365 | 0.865 | 0.500 | 0.1257 | 35.02 | 117.57 |
| | 318 | 0.0022 | 0.1207 | 0.0464 | –0.1803 | –0.3952 | –0.3430 | 0.389 | 0.886 | 0.496 | 0.2496 | | |
| | 333 | 0.0128 | 0.0839 | 0.0495 | –0.1293 | –0.2856 | –0.0134 | 0.372 | 0.873 | 0.502 | 0.4387 | | |
La15.5Mg6Ni78.5 | Absorption | 303 | 0.0830 | 0.0152 | –0.1082 | –0.0313 | –0.3243 | 0.0215 | 0.085 | 0.733 | 0.648 | 0.3195 | –27.23 | –99.33 |
| | 318 | 0.0730 | 0.0591 | 0.1128 | –0.0815 | –0.6188 | 0.0080 | 0.088 | 0.695 | 0.607 | 0.5038 | | |
| | 333 | 0.0915 | 0.0734 | –0.0211 | –0.0934 | –0.5815 | 0.0075 | 0.107 | 0.715 | 0.608 | 0.8466 | | |
| Desorption | 303 | –0.0932 | 0.0065 | 0.8130 | –0.0462 | –0.0544 | 0.0130 | 0.175 | 0.843 | 0.668 | 0.2152 | 31.39 | 109.97 |
| | 318 | –0.0243 | 0.0195 | 0.3615 | –0.0527 | –0.1009 | 0.0148 | 0.214 | 0.836 | 0.622 | 0.3924 | | |
| | 333 | –0.0387 | 0.0507 | 0.4799 | –0.0800 | –0.1645 | 0.0030 | 0.212 | 0.822 | 0.610 | 0.6605 | | |